The Formation Process Of Hot Galvanizing Layer

- Apr 10, 2018 -

The formation process of hot galvanizing layer.

Galvanized layer formation process is the most out of pure iron substrate and formed between the zinc layer of iron, zinc alloy, the process of workpiece surface formed in hot dip plating of iron - zinc alloy layer, and makes good combination between iron and pure zinc layer, the process can be simply described as follows: when the blacksmith a immersed in molten zinc liquid, zinc first formed in the interface and alpha (heart) solid solution.This is a matrix of metallic iron dissolved in a solid state with zinc atoms forming a crystal, the two metal atoms are fused together, the atom is less attractive.So when zinc in solid solution after reaching saturation, two kinds of zinc iron atom diffusion, spread to (or called infiltration) iron matrix of zinc atom in the lattice matrix migration, gradually formed and iron alloy, and spread to molten zinc liquid iron and zinc in the formation of intermetallic compounds FeZn13, sank into the hot dip galvanized pot is zinc slag.When the workpiece is removed from the zinc-impregnated liquid, it forms a pure zinc layer, which is a hexagon crystal.Its iron content is not greater than 0.003%.