Improve mechanical properties of hot dip galvanizing line.

- Oct 26, 2018 -

 Improve mechanical properties of hot dip galvanizing line.
1. In steelmaking, vacuum treatment is adopted to reduce C, 02 and S in the steel base, because these elements are easy to become crystal nuclei in recrystallization, which causes grain refinement and cannot make the steel soft.
2, in order to obtain deep drawing note structure, galvanized the original plate should be placed on note for decarburizing annealing bell type furnace, annealing temperature is 680 ℃, time of 24 hours, dew point control in - 20 ~ 30 ℃, and finally to - 12 ℃, purposefully increase the moisture content in furnace atmosphere, makes the oxidation of carbon steel, to take off, C reaction is as follows: take off the benefits of C: C + H0 - > CO + H
(1) after decarburization, the carbon content of steel plate decreased from 0.08% to 0.008~0.1%
(2) during decarburization annealing, ALN precipitates out on the grain surface, which imposes certain restrictions on the growth of the grain, so that the grain can only grow in a flattened direction, and finally form a cake shaped grain with good deep-drawing performance.
(3) in the enclosed furnace, the precipitation rate of ALN is basically the same as that of recrystallization; while in the continuous annealing furnace, the recrystallization rate is higher than that of ALN, and the pie shape grain is not used.
3. For the galvanized sheet with mild deep drawing, the method of reducing the running speed of strip steel by 10-25% can be adopted in the continuous furnace to improve the deep-drawing performance.4, for complex deep drawing forming of hot galvanized sheet, the galvanized products of low temperature tempering in the bell type furnace (also known as artificial aging treatment), keep the tempering temperature 250 ~ 280 ℃ and tempering time 24 hours, after tempering to level off, the roughness is in commonly 0.8 ~ 1.4% to eliminate stress, improving mechanical properties of materials, can be decreased the yield platform 2 kg, tensile strength decreased 3 kg, extend the average increased by 3%.
5. For the strip steel with thickness <0.2mm, the belt temperature should be lower than the recrystallization temperature when annealing in line to reach a certain strength. 

.6. For low-alloy high-strength hot galvanized sheet, 0.008~0.04% Ti shall be added to the steel.

And control of Ti/L + N > 7.5 ℃, its action is as follows:

(1) the strength of galvanized sheet can be significantly improved, with 5 s up to 36.1 kg2, b up to 52NENkg2 and HRB up to 75.

(2) Ti can play the role of fixing N and C in steel, so that the steel can play the role of fixing N and C in steel, so that the steel can be out and the steel's endurance can be improved.